| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体质量流动速率 | 230℃,10kg | ASTM D-1238 | 15 | g/10min |
| 熔体质量流动速率 | 230℃,3.8kg | ASTM D-1238 | 4.5 | g/10min | |
| 物理性能 | 比重 | ASTM D-792 | 1.05 | g/cm3 | |
| 模具收缩率 | ASTM D-955 | 0.40-0.60 | % | ||
| 机械性能 | 拉伸模量 | ASTM D-638 | 2200 | MPa | |
| 拉伸屈服强度 | ASTM D-638 | 41.3 | MPa | ||
| 弯曲模量 | ASTM D-790 | 2200 | MPa | ||
| 弯曲屈服强度 | ASTM D-790 | 65.5 | MPa | ||
| IZOD缺口冲击强度 | -40℃,3.20mm | ASTM D-256 | 64.1 | J/m | |
| IZOD缺口冲击强度 | 23℃,3.20mm | ASTM D-256 | 347 | J/m | |
| 洛氏硬度 | ASTM D-785 | 109 | R scale | ||
| 热性能 | 热变形温度 | 0.45MPa，未退火，12.7mm | ASTM D-648 | 96.0 | ℃ |
| 热变形温度 | 0.45MPa，退火，12.7mm | ASTM D-648 | 102 | ℃ | |
| 热变形温度 | 1.80MPa，未退火，12.7mm | ASTM D-648 | 85.0 | ℃ | |
| 热变形温度 | 1.80MPa，退火，12.7mm | ASTM D-648 | 97.0 | ℃ | |
| 维卡软化点 | ASTM D-1525 | 106 | ℃ | ||
| CLTE | ASTM D-696 | 0.000090 | cm/cm℃ | ||
| 燃烧性 | 1.50mm | UL 94 | HB | ||
| 燃烧性 | 3.0mm | UL 94 | HB | ||
| 光学性能 | 光泽度 | 60℃ | ASTM D-253 | 90 | |
免责声明：当前页为 供应ABS 633 英力士产品信息展示页，该页所展示的 供应ABS 633 英力士产品信息及价格等相关信息均有企业自行发布与提供， 供应ABS 633 英力士产品真实性、准确性、合法性由店铺所有企业完全负责。世界工厂网对此不承担任何保证责任，亦不涉及用户间因交易而产生的法律关系及法律纠纷，纠纷由会员自行协商解决。
友情提醒：世界工厂网仅作为用户寻找交易对象，就货物和服务的交易进行协商，以及获取各类与贸易相关的服务信息的渠道。为避免产生购买风险，建议您在购买相关产品前务必确认供应商资质及产品质量。过低的价格、夸张的描述、私人银行账户等都有可能是虚假信息，请您谨慎对待，谨防欺诈，对于任何付款行为请您慎重抉择。
投诉方式：fawu@gongchang.com是处理侵权投诉的专用邮箱，在您的合法权益受到侵害时，请将您真实身份信息及受到侵权的初步证据发送到该邮箱，我们会在5个工作日内给您答复，感谢您对世界工厂网的关注与支持！
(c)2008-2024 世界工厂网V3.6 All Rights Reserved 豫ICP备2024066506号