| 规格级别 | 注塑级 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 加工条件 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 230℃/3.8kg | ASTM D-1238 | 6.0 | g/10min |
| 物理性能 | 比重 | ASTM D-792 | 1.04 | g/cm3 | |
| 模具收缩率 | Flow | ASTM D-955 | 0.40-0.70 | % | |
| 机械性能 | 拉伸模量 | 3.18mm | ASTM D-638 | 1790 | MPa |
| 拉伸屈服强度 | 3.18mm | ASTM D-638 | 41.4 | MPa | |
| 屈服伸长率 | 3.18mm | ASTM D-638 | 3.0 | % | |
| 弯曲模量 | 3.18mm | ASTM D-790 | 2000 | MPa | |
| 弯曲强度 | 3.18mm | ASTM D-790 | 58.6 | MPa | |
| charpy缺口冲击强度 | 23℃ | ISO 179/1eA | 16.0 | KJ/m2 | |
| charpy缺口冲击强度 | -30℃ | ISO 179/1eA | 8.00 | KJ/m2 | |
| IZOD缺口冲击强度 | -18℃,3.18mm | ASTM D-256 | 80.1 | J/m | |
| IZOD缺口冲击强度 | 23℃,3.18mm | ASTM D-256 | 160 | J/m | |
| 热性能 | 热变形温度 | 0.45MPa，未退火 | ASTM D-648 | 90.6 | ℃ |
| 热变形温度 | 0.45MPa | ASTM D-648 | 89.0 | ℃ | |
| 热变形温度 | 1.80MPa，未退火 | ASTM D-648 | 76.7 | ℃ | |
| 热变形温度 | 1.80MPa，退火 | ASTM D-648 | 80.0 | ℃ | |
| 维卡软化温度 | ASTM D-1525 | 104 | ℃ | ||
| CLTE | Flow | ASTM D-696 | 0.000078 | cm/cm/℃ | |
免责声明：当前页为 ABS 342 EZ 348 美国陶氏产品信息展示页，该页所展示的 ABS 342 EZ 348 美国陶氏产品信息及价格等相关信息均有企业自行发布与提供， ABS 342 EZ 348 美国陶氏产品真实性、准确性、合法性由店铺所有企业完全负责。世界工厂网对此不承担任何保证责任，亦不涉及用户间因交易而产生的法律关系及法律纠纷，纠纷由会员自行协商解决。
友情提醒：世界工厂网仅作为用户寻找交易对象，就货物和服务的交易进行协商，以及获取各类与贸易相关的服务信息的渠道。为避免产生购买风险，建议您在购买相关产品前务必确认供应商资质及产品质量。过低的价格、夸张的描述、私人银行账户等都有可能是虚假信息，请您谨慎对待，谨防欺诈，对于任何付款行为请您慎重抉择。
投诉方式：fawu@gongchang.com是处理侵权投诉的专用邮箱，在您的合法权益受到侵害时，请将您真实身份信息及受到侵权的初步证据发送到该邮箱，我们会在5个工作日内给您答复，感谢您对世界工厂网的关注与支持！
(c)2008-2024 世界工厂网V3.6 All Rights Reserved 豫ICP备2024066506号