热塑性橡胶SEBS

SEBS Thermoplastic elastomer

热塑性橡胶SEBS产品耐老化性能优良，广泛用于高弹性制品、包履材料（工具手柄）、聚合物改性、胶粘剂与密封剂、医疗器械、电线电缆的填充料等。

SEBS is of excellent aging resistance and used for highly elastic products, packing material (tool handles) polymer modification,adhesives,sealant,meddical treatment equipment and fillers of wires and cables.

SEBS具有较好的耐温性能，其脆化温度≤－60℃，*时使用温度达到149℃，在氧气气氛下其分解温度大于270℃。SEBS有优异的耐老化性能，在人工加速老化箱中老化一星期其性能的下降率小于10%。SEBS有优良的电性能，其介电损耗在一千赫为1.3×10，一兆赫为2.3×10；体积电阻是一分钟9×10Ω-cm,二分钟2×10Ω-cm。SEBS具有良好的溶解性能和共混性能，其溶解度参数在7.2-7.6之间。

SEBS is of good temperature endurance with brittle temperature lower than-60℃and highest service temperature at149℃,Under oxygen surround. The decomposing point is higher than270℃.SEBS has excellent aging resistance and the drop rate of its performance is less than 10% after being aged in the artificial aging accelerator for one week.

SEBS is also very good at electrical property Its dielectric loss is 1.3×10 at 1KHZ and 2.3×10 at 1MHZ; its volume resistance is 9×10Ω-cm one minute and 2×10Ω-cm two minutes. SEBS has good solubility and co-mixing capacity with solubility between 7.2～7.6.

主要牌号有：YH-501、YH-502、YH-503、YH-561、YH-602

注：*20%甲苯溶液 ^10%甲苯溶液

● SEBS通过与聚丙烯、环烷油或氢化环烷油、白油等混合可生产邵A0-95度的弹性体，此类弹性体有优异的表面质感和耐候抗老化性能，可广泛用于软接触材料如手柄、文具、玩具、运动器材的握手、密封条、电线电缆、牙刷柄及其它包覆材料等。

● SEBS通过化学改性或共混于增韧尼龙（PA6）、聚碳酸脂（PC）聚苯醚（PPO）聚脂（PET、PBT）、聚丙烯（PP）作塑料共混的相容剂等。

● SEBS可用作工程塑料的相容剂，如作PE与PS相容剂。

● SEBS与聚丙烯、白油阻燃剂等共混可用于生产电线电缆的护套或外表皮。

● SEBS通过与碳五等石油树脂配合可用于生产**粘胶剂、密封剂。

● SEBS具有耐老化性能，可直接用于润滑油粘度指数稳定剂。