高性能蜂窝板/不锈钢粘接方案—3M DP7250FR

高性能蜂窝板/不锈钢粘接方案—DP7250FR

轨道交通 不锈钢及铝蜂窝结构的门板地板粘接 各类金属及复合材料结构粘接 铁路行业认证，阻燃配方

建筑 金属加强筋粘接 大面积金属面板粘接 轻量化蜂窝结构及夹心结构粘接

一般工业 **的高温强度和耐候性 增韧、耐冲击

13. All Rights Reserved.21 February 2020 © 3M 3M Confidential.

3M Internal Use only

Typical uncured physical properties

DP7250FR系列

DP7250FRBlack • 重量比：DP7250 FR Black WR • 体积比：DP7250 FR Black VR

DP7250 FR （淡黄色）

base (Part B) Hardener (Part A)

base Modified Epoxy Modified Amine

Color Off white Black

Viscosity (Brookfield DV2 at 23C, #6 20rpm)

87600 34400

Density (g/cm3) 1.34 1.12

Mix ratio

By weight or By volume

2 1

Work life (23C) 60 min for 20g

Cure condition 60C 1h + 23C 24h

高性能蜂窝板/不锈钢粘接方案—DP7250FR

14. All Rights Reserved.21 February 2020 © 3M 3M Confidential.

3M Internal Use only

Property DP7250 FR Black

Color Black

Hardness (ASTM D 2240) Shore D 60-80

Density after curing (g/cm3) 1.30

Tensile strength (T block, MPa) 19

Tensile strength, (MPa) 35

Elongation 5%

Storage modulus (23C, MPa) 1800

Glass Transition Temperature (Tg) by DMA (C) 69

Typical cured physical properties 高性能蜂窝板/不锈钢粘接方案—DP7250FR

15. All Rights Reserved.21 February 2020 © 3M 3M Confidential.

3M Internal Use only

3M DP7250 FR Black performance

Test Item: Overlap shear strength

• Adhesives: DP7250 FR Black WR, DP7250 FR Black VR • Test substrates: Aluminum 6063 Stainless steel 304 • Cure condition: 60℃ 1h, 23℃24h • Aging condition: 85℃, 85% 5 days

20.1

22.723.4

25.4

17.5

23.723.6

25.8

20.4

25.2

21.6

22.9

0

5

10

15

20

25

30

7250 WR 7250 VR

OLS (Mpa)

Al-Al Al-Al 85C 85%RH -5d Al-SS Al-SS 85C 85%RH -5d SS-SS SS-SS 85C 85%RH -5d

DP7250 FR Black WR and DP7250 FR Black VR both show high bonding strength and good aging performance on Al-Al, Al-SS and SS-SS adhesion with cohesive failure mode.

高性能蜂窝板/不锈钢粘接方案—DP7250FR

16. All Rights Reserved.21 February 2020 © 3M 3M Confidential.

3M Internal Use only

3M DP7250 FR Black performance

Test Item: Bell peel 

• Adhesives: DP7250 FR Black WR vs. DP7250 FR Black VR • Test substrates: Aluminum 6063 Aluminum sheet Stainless steel sheet • Cure condition: 60℃ 1h, 23℃24h • Aging condition: 85℃, 85% 5 days 

7.4

5.7

9.7

9.2

2

1

2.8

1.4

0

2

4

6

8

10

12

7250 WR 7250 VR

Bell peel (N/mm)

Al-Al Al-Al 85C 85%RH -5d Al-SS Al-SS 85C 85%RH -5d

DP7250 FR Black WR and DP7250 FR Black VR both show high peel strengthand good aging performance on Al-Al sheet and  Al-SS sheet adhesion with cohesive failure mode. DP7250 FR Black WR is recommended for applications required high peel performance. 

高性能蜂窝板/不锈钢粘接方案—DP7250FR

17. All Rights Reserved.21 February 2020 © 3M 3M Confidential.

3M Internal Use only

3M DP7250 FR Black performance

Test Item: Drum peel 

• Adhesives: DP7250 FR Black WR • Test substrates: Aluminum Aluminum honeycomb Stainless steel Stainless steel honeycomb • Cure condition: 60℃ 1h, 23℃24h

69

45

0

20

40

60

80

7250 WR

Drum peel (N/mm·mm)

Al-AlHC SS-SSHC

DP7250 FR Black WR shows high peel strength on Al-AlHCand  SS-SSHC adhesion with cohesive failure mode. 

高性能蜂窝板/不锈钢粘接方案—DP7250FR

18. All Rights Reserved.21 February 2020 © 3M 3M Confidential.

3M Internal Use only

Testitem 7250 WR 7250 VR 7240 DP460NS LSB60

OLS (MPa)

Al-Al 20.1 CF 22.7 CF 19.3 CF 20.0 AF 22.6 CF Al-Al85C 85%RH -5d 23.4 CF 25.4 CF 20.6 CF 26.8 AF 31.1 CF Al-SS 17.5 CF 23.7 CF 15.4 CF 24.0 AF 21.2 CF/AF Al-SS85C 85%RH -5d 23.6 CF 25.8 CF 17.4 CF/AF 24.9 AF 22.3 CF/AF SS-SS 20.4 CF 25.2 CF 12.5 CF 24.3 CF/AF 24.4 CF/AF SS-SS 85C 85%RH -5d 21.6 CF 22.9 CF 15.7 CF/AF 20.9 AF 22.4 CF/AF

20.1

22.7

19.3 20 22.623.4 25.4 20.6 26.8

31

17.5

23.7

15.4

24

21.2

23.6

25.8

17.4

24.9

22.3

20.4

25.2

12.5

24.3 24.4

21.6

22.9

15.7

20.9

22.4

0

5

10

15

20

25

30

35

7250 WR 7250 VR 7240 DP460NS LSB60

OLS (Mpa)

Al-Al Al-Al 85C 85%RH -5d Al-SS Al-SS 85C 85%RH -5d SS-SS SS-SS 85C 85%RH -5d

Test Background

Test Item: Overlap shear strength

• Adhesives: DP7250 FR Black WR, DP7250 FR Black VR, 7240 B/A FR, DP460NS Off-white,  LSB60 • Test substrates: Aluminum 6063 Stainless steel 304 • Cure condition: 60℃ 1h, 23℃ 24h • Aging condition: 85℃, 85% 5 days 

高性能蜂窝板/不锈钢粘接方案—DP7250FR

19. All Rights Reserved.21 February 2020 © 3M 3M Confidential.

3M Internal Use only

Testitem 7250 WR 7250 VR 7240 DP460NS LSB60

Bell peel (N/mm)

Al-Al 7.4 CF 5.7 CF 7.4 CF 4.9 AF 7.1  (SHOCK) Al-Al85C 85%RH -5d 9.7 CF 9.2 CF 8.1 AF/CF 6.0 AF 6.7 (SHOCK) Al-SS 2.0 CF 1.0 CF 2.7 CF 0.3 AF 0.5 AF Al-SS 85C 85%RH -5d 2.8 CF 1.4 AF 2.6 CF/AF 0.4 AF 0.4 AF

7.4

5.7

7.4

4.9

7.1

9.7

9.2

8.1

6

6.7

2

1

2.7

0.3 0.5

2.8

1.4

2.6

0.4 0.4

0

2

4

6

8

10

12

7250 WR 7250 VR 7240 DP460NS LSB60

Bell peel (N/mm)

Al-Al Al-Al 85C 85%RH -5d Al-SS Al-SS 85C 85%RH -5d

Test Background

Test Item: Bell peel 

• Adhesives: DP7250 FR Black WR, DP7250 FR Black VR, 7240 B/A FR, DP460NS Off-white, LSB60 • Test substrates: Aluminum 6063 Aluminum sheet Stainless steel sheet • Cure condition: 60℃@1 h, 23℃@24 h • Aging condition: 85℃, 85%@ 5 days 

高性能蜂窝板/不锈钢粘接方案—DP7250FR

20. All Rights Reserved.21 February 2020 © 3M 3M Confidential.

3M Internal Use only

• 高温120℃-150℃固化 • 主要用于粘接金属、玻璃、陶瓷，木材，塑料等，应用于多种特殊要求行业 • 在室温和高温下均具有良好的抗塌陷性能 • 粘接处具有极强本体强度和粘接强度，抗冲击能力优异 • 具有**的高温性能，在高温高湿条件下优异的性能 耐