| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 收缩率 | 干 | 旭化成方法 | 1.3-2.0 | % |
| MD2.0mm | ASTMD995 | 1.3 | % | |
| TD2.0mm | ASTMD995 | 2.0 | % | |
| 吸水率 | (23°C,24hr) | ASTMD570 | 2.5 | % |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 断裂伸长率 | 23°C | ASTMD638 | 50 | % |
| ASTM D638/ISO 527 | 50 | % | ||
| 断裂延伸率 | 干(湿) | ASTM D-638 | 50(250) | % |
| 抗挠强度 | 干(湿) | ASTM D-790 | 118(54) | Mpa |
| 抗挠系数 | 干(湿) | ASTM D-790 | 2.8(1.2) | GPa |
| 拉伸强度 | 干(湿) | ASTM D-638 | 79(57) | Mpa |
| 23°C | ASTMD638 | 79 | Mpa | |
| 洛氏硬度 | 干(湿) | ASTM D-785 | 120(108) | R scale |
| 干(湿) | ASTM D-785 | 80(55) | M Scale | |
| 磨耗率 | 湿 | ASTM D-1044 | 7 | |
| 弯曲模量 | 23°C | ASTMD790 | 2800 | Mpa |
| ASTM D790/ISO 178 | 2790 | kg·cm/cm(J/M)ft·lb/in | ||
| 弯曲强度 | ASTM D790/ISO 178 | 118 | kg·cm/cm(J/M)ft·lb/in | |
| 23°C | ASTMD790 | 118 | Mpa | |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 39 | J/m |
| 悬臂梁式缺口冲击强度 | 干(湿) | ASTM D-256 | 39(147) | J/m |
| Charpy冲击强度 | ASTM D256/ISO 179 | 39 | kg·cm/cm(J/M)ft·lb/in |
免责声明：当前页为 1300S旭化成PA66产品信息展示页，该页所展示的 1300S旭化成PA66产品信息及价格等相关信息均有企业自行发布与提供， 1300S旭化成PA66产品真实性、准确性、合法性由店铺所有企业完全负责。世界工厂网对此不承担任何保证责任，亦不涉及用户间因交易而产生的法律关系及法律纠纷，纠纷由会员自行协商解决。
友情提醒：世界工厂网仅作为用户寻找交易对象，就货物和服务的交易进行协商，以及获取各类与贸易相关的服务信息的渠道。为避免产生购买风险，建议您在购买相关产品前务必确认供应商资质及产品质量。过低的价格、夸张的描述、私人银行账户等都有可能是虚假信息，请您谨慎对待，谨防欺诈，对于任何付款行为请您慎重抉择。
投诉方式：fawu@gongchang.com是处理侵权投诉的专用邮箱，在您的合法权益受到侵害时，请将您真实身份信息及受到侵权的初步证据发送到该邮箱，我们会在5个工作日内给您答复，感谢您对世界工厂网的关注与支持！
(c)2008-2025 世界工厂网V3.6 All Rights Reserved 豫ICP备2024066506号